Polyvinyl chloride (PVC) is one of the five thermoplastic universal plastics, has a wide range of applications in various fields, because of its outstanding durability and comprehensive performance advantages, as well as unique technical and economic characteristics, broad prospects for development. But it has poor thermal stability, low toughness at room temperature and is easy to fracture when impacted. Manufacturing high-performance PVC materials, especially high toughness PVC alloy, need to add toughening ingredients, that is, impact resistance modifier; Polyvinyl chloride belongs to polar polymer, melt viscosity, low thermal stability, not easy to high temperature plasticizing, for high strength non-plasticizing polyvinyl chloride material processing, the need to use plasticizing processing additives, so that the processing performance is improved.
This study aimed at the requirement of high performance of PVC material, the use of acrylic monomers, respectively with core-shell structure was synthesized polyacrylic ester (ACR), impact modifiers and polyacrylate plasticizing processing AIDS, by acrylic ester with chitosan (CTS) graft copolymerization, obtain copolymerization modified additives with shock and antibacterial functions. In this study, butyl acrylate (BA), methyl methacrylate (MMA) as soft and hard monomers, potassium persulfate (KPS) as initiator, through the method of seed emulsion polymerization synthesis of soft core and hard shell anti-impact modifier I-ACR, chitosan (CTS) as a natural antibacterial agent, contains a variety of functional groups, highly reactive, can be oxidized, reduced, Grafting and other reactions. By comparing the properties of various chitosan, water-soluble chitosan with good properties was selected. Cerium ammonium nitrate (CAN) was used to initiate chitosan to produce free radicals, and graft copolymerization reaction with MMA occurred.
Ο αντι-τροποποιητής κρούσης CTS-ACR συντέθηκε με συμπολυμερισμό μοσχεύματος μονομερών χιτοζάνης και ακρυλικού με αντιβακτηριακές ιδιότητες. Λαμβάνοντας ως δείκτες στερεό περιεχόμενο γαλακτώματος, ρυθμό γέλης, ρυθμό μετατροπής μονομερών και μηχανικές ιδιότητες του ACR στο PVC, τις επιδράσεις του γαλακτωματοποιητή, του εκκινητή και της δόσης, της αναλογίας τροφοδοσίας σκληρού και μαλακού μονομερούς, της θερμοκρασίας πολυμερισμού και του χρόνου αντίδρασης στις ιδιότητες ACR των δύο Τα συστήματα διερευνήθηκαν για τον προσδιορισμό των καλύτερων συνθηκών σύνθεσης και την προσπάθεια ξήρανσης της μεθόδου που είναι εύκολο να γίνει σκόνη. Η δομή του ACR χαρακτηρίστηκε με υπέρυθρη φασματοσκοπία (IR), οι θερμοκρασίες πολλαπλής μετάπτωσης γυαλιού διερευνήθηκαν με θερμιδομετρία διαφορικής θερμικής σάρωσης (DSC) και το μέγεθος σωματιδίων και η κατανομή του γαλακτώματος μετρήθηκαν με αναλυτή μεγέθους σωματιδίων λέιζερ. Το βοήθημα επεξεργασίας P-ACR με υψηλό μοριακό βάρος συντέθηκε με πολυμερισμό γαλακτώματος με κύριο δείκτη το χαρακτηριστικό ιξώδες.
The preparation and properties of P - ACR test: with BA, MMA as the monomer, potassium persulfate as initiator, synthesis of P - ACR resin by using the method of emulsion polymerization, with P - characteristic viscosity of ACR resin as the main index, the various factors in the emulsion polymerization system and the relationship between polymer molecular weight, get used to this system the following conclusions: (1) appropriate emulsifier The molecular weight of P-ACR can be increased by adding more emulsifiers, but too much emulsifier is not conducive to the increase of molecular weight. (2) The increase of initiator concentration will decrease the molecular weight of P-ACR; (3) Low polymerization temperature is beneficial to increase the molecular weight of P-ACR; (4) Prolonging the reaction time can increase the molecular weight of P-ACR under the improved polymerization process; (5) With the increase of BA feed quantity, p-ACR molecular quantity increases. Three kinds of polyacrylate polymers were blended with polyvinyl chloride to obtain the blend material. The effects of mixing time and temperature on mechanical properties of PVC/ACR blends were tested.
Η αντοχή στην κρούση, οι ιδιότητες εφελκυσμού και η αντοχή στη θερμότητα του PVC τροποποιημένου με διαφορετικό τροποποιητή κρούσης ACR δοκιμάστηκαν. Η διασπορά του μίγματος παρατηρήθηκε με ηλεκτρονικό μικροσκόπιο σάρωσης και παρατηρήθηκε το εύθραυστο ή όλκιμο κάταγμα του τμήματος κρούσης του μίγματος. Οι δύο τροποποιητές κρούσης ACR μπορούν προφανώς να βελτιώσουν την αντοχή σε κρούση του PVC. Με την αύξηση του αριθμού των ACR, η σκληρότητα του PVC αυξάνεται και οι μηχανικές ιδιότητες του I-ACR είναι ελαφρώς καλύτερες από αυτές του CTS-ACR. Οι αντιβακτηριακές ιδιότητες των υλικών PVC/CTS-ACR δοκιμάστηκαν και διαπιστώθηκε ότι το υλικό του μείγματος είχε εξαιρετικές αντιβακτηριακές ιδιότητες. Διαπιστώθηκε ότι το P-ACR μπορεί προφανώς να βελτιώσει την ιδιότητα επεξεργασίας του PVC. Όσο περισσότερο P-ACR, τόσο καλύτερη είναι η ιδιότητα επεξεργασίας του PVC.